Gd~（3＋）掺杂SiO_2/TiO_2的制备及降解活性（英文）

采用溶胶-凝胶法制备Gd3＋掺杂SiO2/TiO2（Gd3＋-SiO2/TiO2,GST）。用X射线衍射（X-ray diffraction,XRD）仪、热重-差热分析仪、紫外-可见分光光度计（ultraviolet-visible spectrophotometry,UV-Vis）及X射线光电子分光仪（X-ray p...     

Nest-like structures of Sr doped Bi2WO6: Synthesis and enhanced photocatalytic properties

A series of Sr-doped Bi₂WO₆ with three-dimensional (3D) nest-like structures were synthesized through simple hydrothermal route and characterized by XRD, FESEM, TEM, XPS, UV-vis DRS, etc. Morphology observation revealed that the as-synthesized Bi₂WO₆ were self-assembled three-dimensional (3D) nest-like structures, which were constructed from nanoplates. UV-vis diffuse reflectance spectra indicated that the samples had absorption in both UV and visible light areas. Their photocatalytic activities were evaluated by photodegradation of rhodamine B (RhB) under UV and visible light irradiation (λ > 420 nm). The photocatalytic properties were enhanced after Sr doping. Samples subsequently thermal treated at 500 °C showed higher photocatalytic activities. The reasons for the differences in the photocatalytic activities of these nest-like Bi₂WO₆ microstructures were further investigated.     

民族元素在现代首饰设计中的作用

以研究民族元素在设计中的作用为基础,通过对首饰风格特征的分析,研究满足消费者的审美情趣和心理需求的首饰特征;在此基础上研究民族文化对于世界文化的影响,说明民族元素在设计中的重要性并重点以蒙古族元素为例,研究蒙古族元素的特征及其在首饰设计中的应用元素,并在此基础上设计出以蒙古元素为表现特征的首饰。     

Sb掺杂Sn_2S_3薄膜的制备及光学特性

真空蒸发制备Sb掺杂Sn2S3多晶薄膜(玻璃衬底),研究不同比例Sb掺杂对Sn2S3薄膜的结构、表面形貌、化学组分及光学特性的影响。实验给出5%掺Sb的薄膜经380℃热处理30min(氮气保护)得到正交晶系的Sn2S3∶Sb多晶薄膜,薄膜表面颗粒大小均匀,膜面致密有轻微颗粒聚集现象。薄膜体内Sn与S化学计量比为1∶1.49,掺Sb后为1∶0.543,薄膜中Sn、S、Sb分别以Sn2+、Sn4+、S2-、Sb5+存在。纯Sn2S3薄膜的光透过率在350~500nm波长范围内基本为零,随着波长增大,光透过率增加,其直接光学带隙为2.2eV,吸收边为564nm;掺Sb后薄膜的光透率明显降低,光学带隙为1.395eV比未掺杂时减小0.805eV,吸收边发生红移为889nm。     

大直径重掺硅单晶工艺研究

重掺单晶一些独有的特性,能有效解决目前集成电路面临的一些难题。对大直径重掺硅单晶生长过程中的一些工艺进行了研究,主要包括掺杂方式和拉速设定两个方面,通过实验分析,选取了适宜的掺杂方式与拉速,最终生长出外形良好,符合电阻率目标要求的单晶。     

镁合金表面铬掺杂类金刚石薄膜的制备与性能研究

本文利用阳极层离子束混合磁控溅射技术在AZ31镁合金表面制备了类金刚石涂层（DLC）和Cr掺杂DLC膜（Cr-DLC）,并利用Raman光谱、残余应力仪、划痕仪、摩擦磨损仪和电化学工作站等,对薄膜的碳结构、残余应力、结合力、摩擦学性能和耐腐蚀性进行了研究。结果表明：相比纯DLC膜,Cr-DLC膜具有较低的残余应力,较高的膜/基结合力。Cr-DLC膜能显著提高镁合金的抗摩擦磨损性能,但对改善镁合金耐腐蚀性能影响不大。     

水解工艺Yb3＋/Al3＋共掺石英玻璃的研制及特性表征

利用四氯化硅(SiCl₄)水解掺杂法结合高 频等离子体粉末熔融技术制备了Yb3＋/Al3＋共掺石英玻璃,并利用 X射 线衍射(XRD)、傅里叶变换红外(FTIR)光谱分析和热膨胀分析等对所制备玻璃样品的结 构特性、物理特性和光谱特 性进行了表征。结果表明,制备的Yb3＋/Al3＋共掺石英玻璃的密度和折 射率值与纯石英玻璃相接近,并且呈现出 较好的玻璃态,其热膨胀系数为2.87×10－6,具有较好的Yb3＋和Al 3＋掺杂均匀性,以及Yb3＋典型的吸 收特性和发射特性,表明采用本文方法制备的Yb3＋/Al3＋共掺石英玻璃 已具备成为大功率激光材料的潜质。     

固相合成锂离子电池正极材料LiMn_(1-x)Fe_xPO_4/C的结构与电化学性能

以葡萄糖为碳源,对LiH2PO4、MnCO3、FeC2O4与葡萄糖等反应物进行湿法球磨,随后在750℃温度下煅烧,通过固相反应实现对LiMnPO4的铁离子掺杂和碳包覆改性,得到锂离子电池正极材料LiMn1-xFexPO4/C(x=0、0.05、0.10、0.15、0.20)。利用X射线衍射(XRD),扫描电镜(SEM)及电化学测试等手段研究铁离子掺杂量对磷酸锰锂的晶体结构、微观形貌与电性能的影响。结果表明,LiMn0.9Fe0.1PO4/C结晶度良好,颗粒较均匀细小,具有较好的电化学性能,0.05C倍率下的首次放电比容量达到110(mA·h)/g,经过30次循环后,放电比容量约80(mA·h)/g。     

Well‐Combined Magnetically Separable Hybrid Cobalt Ferrite/Nitrogen‐Doped Graphene as Efficient Catalyst with Superior Performance for Oxygen Reduction Reaction

Catalysts with low‐cost, high activity and stability toward oxygen reduction reaction (ORR) are extremely desirable, but its development still remains a great challenge. Here, a novel magnetically separable hybrid of multimetal oxide, cobalt ferrite (CoFe₂O₄), anchored on nitrogen‐doped reduced graphene oxide (CoFe₂O₄/NG) is prepared via a facile solvothermal method followed by calcination at 500 °C. The structure of CoFe₂O₄/NG and the interaction of both components are analyzed by several techniques. The possible formation of Co/Fe N interaction in the CoFe₂O₄/NG catalyst is found. As a result, the well‐combination of CoFe₂O₄ nanoparticles with NG and its improved crystallinity lead to a synergistic and efficient catalyst with high performance to ORR through a four‐electron‐transfer process in alkaline medium. The CoFe₂O₄/NG exhibits particularly comparable catalytic activity as commercial Pt/C catalyst, and superior stability against methanol oxidation and CO poisoning. Meanwhile, it has been proved that both nitrogen doping and the spinel structure of CoFe₂O₄ can have a significant contribution to the catalytic activity by contrast experiments. Multimetal oxide hybrid demonstrates better catalysis to ORR than a single metal oxide hybrid. All results make the low‐cost and magnetically separable CoFe₂O₄/NG a promising alternative for costly platinum‐based ORR catalyst in fuel cells and metal‐air batteries.     

Wettability and biomineralisation of laser cladded Si doped TiCN biocoating

Surface textured Si doped TiCN coatings were synthesised on Ti–6Al–4V alloy by laser cladding technique. Phase constituent examination by X-ray diffraction revealed the formation of similar phases of TiC_0.2N_0.8 and Ti₅Si₄ within all coated samples. Laser coated samples presented much higher surface free energy compared to Ti–6Al–4V control due to the textured structure, which in turn demonstrated a better wettability and improved biomineralisation. Variation of silica content presented no significant influence on surface free energy, indicating that the silica content can be varied in a large range. The mineralised samples obtained after immersion in simulated body fluid were characterised to understand the mechanism and kinetics of Ca–P precipitation. The results confirmed that the precipitation kinetics of Ca–P was influenced by the substitution of silica.